Eagle 636 Hardfacing Welding Rod | 60–63 HRC Severe Abrasion Electrode

Eagle 636 is recommended for:

Earth augers
Bucket teeth
Buckets
Bucket lips
Mixer paddles
Ripper teeth
Screw conveyors
Compactors
Mill hammers
Scraper sides
Mining equipment

Designed for components exposed to severe abrasive wear with moderate impact.

Use AC or DC Reverse [+] Polarity. Use the grinding method or remove fatigued metal using the Eagle 188.
Use lowest effective amperage while maintaining a short arc length making either stringer beads or weave beads with a maximum of two layers of weld deposit.

Eagle 636 is a high-deposition hardfacing electrode engineered for severe abrasive wear applications.

With a deposited hardness of approximately 60–63 Rockwell C, Eagle 636 provides excellent resistance to wear while maintaining enough toughness for applications that also experience moderate impact.

Its high deposition rate makes it especially effective for rebuilding and protecting larger wear surfaces where faster application can reduce welding time and downtime.

Why Eagle 636?

Severe abrasion resistance — 60–63 HRC deposit provides excellent protection against aggressive abrasive wear.

High deposition rate — designed to put down more hardfacing efficiently on larger components and wear surfaces.

Built for heavy equipment — ideal for buckets, augers, ripper teeth, screw conveyors, mining equipment and other heavily worn components.

Tough wear protection — combines severe abrasion resistance with enough impact resistance for demanding industrial applications.

Current: AC or DC Reverse [+] Polarity

Sizes: Inches 1/8, 5/32, 3/16
mm 3.25, 4.00, 5.00
Amperage: 70 - 125, 100 - 120, 130 - 160